ABS

ABS LNP™ STAT-KON™ A3000T SABIC INNOVATIVE US

248

Unit Price:US$ 3,341 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Antistatic｜transparent
Application Areas:Electronic and electrical components｜Automotive components
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Dart impact	23°C, Energy at Peak	ASTM D3763	32.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2060 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2010 Mpa
tensile strength	Yield3	ASTM D638	39.0 Mpa
	tensile strength	Yield	ISO 527-2/5	38.0 Mpa
		tensile strength	Break3	ASTM D638	36.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	31.0 Mpa
elongation	Yield3	ASTM D638	3.1 %
	elongation	Yield	ISO 527-2/5	3.0 %
		elongation	Break3	ASTM D638	6.0 %
		elongation	elongation	Break	ISO 527-2/5	24 %
Bending modulus	50.0 mm Span4	ASTM D790	2090 Mpa
Bending modulus	Bending modulus	--5	ISO 178	1980 Mpa
bending strength	--5,6	ISO 178	59.0 Mpa
bending strength	bending strength	Break, 50.0 mm Span4	ASTM D790	65.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			70 to 80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.050 to 0.10 %
Temperature at the rear of the barrel			180 to 195 °C
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the front of the material cylinder			205 to 215 °C
Processing (melt) temperature			200 to 210 °C
Mold temperature			10 to 50 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	88.0 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Bf	91.0 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	76.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	76.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	9.3E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	9.3E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.0E-4 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow : 24hr	ASTM D955	0.40 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 24hr	ASTM D955	0.50 %
Water absorption rate	24 hr, 50% RH	ASTM D570	1.1 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1.0E+9 - 1.0E+11 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS LNP™ STAT-KON™ A3000T SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet