Plastic Raw Materials
PBT

PBT Cristin®  LW9330 DUPONT USA

230
  • Unit Price:US$ 3,793 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜Low warpage｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% by weight ratio)｜30% filler by weight｜Anti warping｜Good surface performance (glass fiber reinforced
  • Application Areas:Electronic and electrical components｜Automotive Applications｜Industrial applications｜Industrial applications｜Box/Shell/Cover/Set｜Automotive Applications
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-40°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch-40°CISO 179/1eU50 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU55 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A7.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A7.0 kJ/m²
Suspended wall beam without notch impact strength-40°CISO 180/1U45 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U45 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379528 mm/min
UL flame retardant rating0.75mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating0.75mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainBreakISO 527-12.3 %
Tensile modulus23℃ISO 527-19800 MPa
Bending modulus23℃ISO 1788400 MPa
Impact strength of simply supported beam without notch23 ℃, Type 1, EdgewiseISO 17955 KJ/m
Suspended wall beam without notch impact strength-40 ℃, Type 1ISO 18055 KJ/m
Suspended wall beam without notch impact strength23 ℃, Type 1ISO 18065 KJ/m
Impact strength of cantilever beam gap-40 °C, Type 1, Notch AISO 1807 KJ/m
Impact strength of cantilever beam gap23 °C, Type 1, Notch AISO 1807 KJ/m
Tensile modulusISO 527-29800 Mpa
tensile strengthBreakISO 527-2135 Mpa
Tensile strainBreakISO 527-22.3 %
Bending modulusISO 1788400 Mpa
thermal performanceTest ConditionTest MethodTest Result
Melting temperatureISO 3146220 ℃
Hot deformation temperature1.80 Mpa，UnannealedISO 75A-1185 ℃
UL flame retardant rating0.750 mmUL 94HB
UL flame retardant rating1.50 mmUL 94HB
UL flame retardant rating3.00 mmUL 94HB
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A185 °C
Melting temperatureISO 11357-3225 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateFlowISO 294-40.30 %
densityISO 11831.42
Shrinkage rateAcross FlowISO 294-40.60 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.25 %
densityISO 11831.42 g/cm³
melt mass-flow rateISO 113313 g/10min
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113310.0 cm3/10min
Shrinkage rateTDISO 294-40.60 %
Shrinkage rateMDISO 294-40.30 %
Water absorption rateSaturation,23°C,2.00mmISO 621.0 %
MediumDensity1.27 g/cm³
Top out temperature170 °C
SpecificHeatCapacity of Melt1790 J/kg/°C
ThermalConductivityofMelt0.28 W/m/K
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093>1.0E+15 ohms
Compared to the anti leakage trace indexIEC 60112 V
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.