PC LEXAN™  HFD4412 BK1E808 SABIC INNOVATIVE NANSHA

186
  • Unit Price:US$ 2,589 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    22MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility
  • Application Areas:Architectural Applications｜Plastic bag
  • Color:--
  • Grade:Light diffusion level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA8.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA8.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU48 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU43 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D4812830 J/m
Suspended wall beam without notch impact strength-30°C6ISO 180/1U40 kJ/m²
Suspended wall beam without notch impact strength23°C6ISO 180/1U42 kJ/m²
Dart impact23°C, Total EnergyASTM D376321.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.30 mmUL 94HB
Burning wire flammability index2.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0 mmIEC 60695-2-13850 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6386400 Mpa
tensile strengthYield3ASTM D63896.0 Mpa
tensile strengthYieldISO 527-2/5110 Mpa
tensile strengthBreak3ASTM D63896.0 Mpa
tensile strengthBreakISO 527-2/5110 Mpa
elongationYield3ASTM D6383.0 %
elongationYieldISO 527-2/52.8 %
elongationBreakISO 527-2/52.7 %
Bending modulus50.0 mm SpanASTM D7905850 Mpa
bending strengthYield, 50.0 mm SpanASTM D790159 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel265 to 290 °C
Temperature in the middle of the barrel275 to 300 °C
Temperature at the front of the material cylinder290 to 310 °C
Spray nozzle temperature280 to 305 °C
Processing (melt) temperature290 to 310 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648130 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648125 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7ISO 75-2/Af127 °C
Vicat softening temperatureISO 306/B120143 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8313.0E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-23.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8317.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.0E-5 cm/cm/°C
RTI ElecUL 74680.0 °C
RTI ImpUL 74680.0 °C
RTIUL 74680.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123815 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113314.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.10 - 0.30 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.10 - 0.30 %
Water absorption rateSaturation, 23°CISO 620.30 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.12 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.