PPS

PPS FORTRON® 1140L7 SD3002 CELANESE USA

249

Unit Price:US$ 6,730 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
120MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Glass fiber reinforced｜High temperature resistance
Application Areas:fibre｜Bottle cap
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.38 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A	14500 Mpa
tensile strength	Break	ISO 527-2/1A/5	170 Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.6 %
Bending modulus	23°C	ISO 178	14500 Mpa
bending strength		ISO 178	260 Mpa
Compressive modulus		ISO 604	14000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			130 to 140 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			20 to 30 °C
Temperature at the rear of the barrel			290 to 300 °C
Temperature in the middle of the barrel			310 to 320 °C
Temperature at the front of the material cylinder			330 to 340 °C
Spray nozzle temperature			310 to 330 °C
Processing (melt) temperature			330 to 340 °C
Mold temperature			140 to 160 °C
Injection speed			快速
Back pressure			< 3.00 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	270 °C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	200 °C
Glass transition temperature		ISO 11357-2	90.0 °C
Melting temperature		ISO 11357-3	280 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.10 - 0.30 %
Water absorption rate	Saturation, 23°C	ISO 62	0.020 %

Electrical performance	Test Method	Test Result
Surface resistivity	IEC 60093	> 1.0E+15 ohms
Volume resistivity	IEC 60093	> 1.0E+15 ohms·cm
Dielectric strength	IEC 60243-1	26 KV/mm
Compared to the anti leakage trace index	IEC 60112	PLC 4

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale	ISO 2039-2	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.