PC/ABS

PC/ABS CYCOLAC™ LG9000 SABIC INNOVATIVE US

248

Unit Price:US$ 4,045 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°,无织构	ASTM D523	30

impact performance	Test Condition	Test Method	Test Result
Dart impact	-30°C,TotalEnergy	ASTM D3763	33.9 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	40.7 J
Impact strength of cantilever beam gap	23°C	ASTM D256	530 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	320 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	84.8 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2310 Mpa
elongation	Break	ASTM D638	75 %
tensile strength	Yield	ASTM D638	54.5 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI Elec		UL 746	60.0 °C
thermal conductivity		ASTMC177	0.20 W/m/K
Linear coefficient of thermal expansion	TD：-20to150°C	ASTME831	7.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-20to150°C	ASTME831	7.2E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	124 °C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	129 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	107 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	110 °C
Vicat softening temperature		ASTM D15254	129 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C	ASTM D570	0.40 %
Water absorption rate	Water absorption rate	24hr	ASTM D570	0.10 %
Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
melt mass-flow rate	260°C/5.0kg	ASTM D1238	17 g/10min
density		ASTM D792	1.13 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Arc resistance		ASTM D495	PLC6

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.