PC/ABS

PC/ABS LUPOY® HR5007A-KA02 LG GUANGZHOU

409

Unit Price:US$ 3,244 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜High mobility｜High temperature resistance
Application Areas:Automotive sector｜Electronic field｜Electrical field｜Automotive interior parts｜Electrical components
Color:--
Grade:High liquidity level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eU2	NoBreak
	Charpy Notched Impact Strength	23°C	ISO 179/1eU2	NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA2	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	3.20mm	ASTM D790	77.5 Mpa
Bending modulus	3.20mm,InjectionMolded	ASTM D790	2110 Mpa
Tensile modulus		ISO 527-22	2200 Mpa
tensile strength	Yield,3.20mm,Injection	ASTM D638	56.9 Mpa
tensile strength	tensile strength	Yield	ISO 527-22	60.0 Mpa
Tensile strain	Yield	ISO 527-22	4.9 %
Tensile strain	Tensile strain	Break,3.20mm,InjectionMolded	ASTM D638	>100 %
Nominal fracture strain		ISO 527-22	>50 %

thermal performance	Test Condition	Test Method	Test Result
RTI Str	3.0mm	UL 746	60.0 °C
RTI Str	RTI Str	1.6mm	UL 746	60.0 °C
RTI Imp	3.0mm	UL 746	60.0 °C
RTI Imp	RTI Imp	1.6mm	UL 746	60.0 °C
RTI Elec	3.0mm	UL 746	60.0 °C
RTI Elec	RTI Elec	1.6mm	UL 746	60.0 °C
Linear coefficient of thermal expansion	TD	ISO 11359-22	8.3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-22	7.7E-05 cm/cm/°C
Vicat softening temperature	50N	ISO 3062	119 °C
Glass transition temperature		ISO 11357-22	150 °C
Hot deformation temperature	1.8MPa	ISO 75-22	104 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm,InjectionMolded	ASTM D648	113 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/2.16kg	ASTM D1238	5.3 g/10min
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ASTM D1505	18.0 cm3/10min
Shrinkage rate	MD：3.20mm,InjectionMolded	ASTM D955	0.50-0.80 %
Water absorption rate	Saturation	ISO 622	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 600932	3.8E+14 ohms
Hot wire ignition	3.0mm	UL 746	PLC 3
Hot wire ignition	Hot wire ignition	1.6mm	UL 746	PLC 3
High voltage arc tracing rate	PLC	UL 746
High arc combustion index	3.0mm	UL 746	PLC 1
High arc combustion index	High arc combustion index	1.6mm	UL 746	PLC 1
Volume resistivity		IEC 600932	>1.0E+13 ohms·m
Dielectric strength		IEC 60243-12	42 KV/mm
Relative permittivity	1MHz	ASTM D1646	2.80
Dissipation factor	1MHz	ASTM D1646	0.010
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index		ISO 2577

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	114

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.