PA66

PA66 Amilan®  CM3006 TORAY JAPAN

385
  • Unit Price:US$ 4,067 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    214.3MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Thermal stability｜Flame retardant
  • Application Areas:Automotive sector｜Electrical components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-40°C无断裂 --
Impact strength of simply supported beam without notch23°C无断裂 --
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.79mmV-2 --
Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate23℃，24hrASTM D-570无水｜1.2 %
Water absorption rate23℃，24hrASTM D-5703.5%水｜- %
mechanical propertiesTest ConditionTest MethodTest Result
Shear strength23℃ASTM D-7323.5%水｜770 kg/cm2
bending strength80℃ASTM D-790无水｜640 kg/cm2
bending strength80℃ASTM D-7903.5%水｜400 kg/cm2
Bending modulus80℃ASTM D-790无水｜9000 kg/cm2
Bending modulus80℃ASTM D-7903.5%水｜5000 kg/cm2
Rockwell hardness23℃ASTM D-785无水｜119 R-标度
Rockwell hardness23℃ASTM D-7853.5%水｜100 R-标度
Bending modulus23℃ASTM D-790无水｜29000 kg/cm2
Elongation at Break23℃ASTM D-638无水｜90 %
Elongation at Break23℃ASTM D-6383.5%水｜< 200 %
Impact strength of cantilever beam gap-40℃，VNotched1/2ASTM D-256无水｜3.5 kg·cm/cm
Impact strength of cantilever beam gap-40℃，VNotched1/2ASTM D-2563.5%水｜- kg·cm/cm
Bending modulus-40℃ASTM D-790无水｜44000 kg/cm2
Bending modulus-40℃ASTM D-7903.5%水｜42000 kg/cm2
Rockwell hardness23℃ASTM D-785无水｜97 M-标度
Rockwell hardness23℃ASTM D-7853.5%水｜- M-标度
Shear strength23℃ASTM D-732无水｜790 kg/cm2
bending strength-40℃ASTM D-7903.5%水｜1300 kg/cm2
Impact strength of cantilever beam gap23℃，Unnotched1/8无水｜无断裂 kg·cm/cm2
tensile strength23℃，YieldASTM D-6383.5%水｜530 kg/cm2
compressive strength23℃ASTM D-695无水｜910 kg/cm2
compressive strength23℃ASTM D-6953.5%水｜- kg/cm2
bending strength23℃ASTM D-790无水｜1150 kg/cm2
bending strength23℃ASTM D-7903.5%水｜650 kg/cm2
tensile strength80℃，YieldASTM D-638无水｜430 kg/cm2
tensile strength80℃，YieldASTM D-6383.5%水｜400 kg/cm2
Bending modulus23℃ASTM D-7903.5%水｜14000 kg/cm2
tensile strength23℃，YieldASTM D-638无水｜800 kg/cm2
Impact strength of cantilever beam gap23℃，Unnotched1/83.5%水｜- kg·cm/cm2
Impact strength of cantilever beam gap23℃，VNotched1/2ASTM D-256无水｜5 kg·cm/cm
Impact strength of cantilever beam gap23℃，VNotched1/2ASTM D-2563.5%水｜28 kg·cm/cm
tensile strength-40℃，YieldASTM D-638无水｜1150 kg/cm2
tensile strength-40℃，YieldASTM D-6383.5%水｜1100 kg/cm2
bending strength-40℃ASTM D-790无水｜1450 kg/cm2
bending strength-40°C140 MPa
bending strength23°CMPa115 65.0
bending strength80°CMPa65.0 40.0
Compressive stress23°CMPa90.0 --
shear strength23°CMPa80.0 75.0
Taber abraser1000Cyclesmg8.00 --
Friction coefficient vs. Metal0.15to0.20 --
tensile strength-40°C115 MPa
tensile strength23°CMPa80.0 50.0
tensile strength80°CMPa40.0 40.0
Tensile strainYield,23°C%1.5 --
Tensile strainBreak,23°C%25
Bending modulus-40°CMPa4300 4100
Bending modulus23°CMPa2900 1400
Bending modulus80°CMPa900 500
Charpy Notched Impact StrengthASTM D256/ISO 17950 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 1782.8 kg·cm/cm(J/M)ft·lb/in
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature4.6kg/cm2ASTM D-648无水｜220 °C
Hot deformation temperature4.6kg/cm2ASTM D-6483.5%水｜- °C
Melting temperature差示扫描测热计DSC265 °C
specific heat无水｜0.4 Cal/g·℃
specific heat3.5%水｜- Cal/g·℃
Linear coefficient of thermal expansionASTM D-696无水｜9-10 ×10-5cm/cm/℃
Linear coefficient of thermal expansionASTM D-6963.5%水｜- ×10-5cm/cm/℃
UL-94 flame retardant grade1/32"UL 94无水｜V-2
UL-94 flame retardant grade1/32"UL 943.5%水｜-
thermal conductivity无水｜0.21 Kcal/m·hr·℃
thermal conductivity3.5%水｜- Kcal/m·hr·℃
Hot deformation temperature0.45MPa,Unannealed°C220 --
Melting temperature°C265 --
Linear coefficient of thermal expansionMDcm/cm/°C9.0E-5到1.0E-4 --
specific heatJ/kg/°C2100 --
thermal conductivityW/m/K0.32 --
Combustibility (rate)UL 94V-2
Hot deformation temperatureHDTASTM D648/ISO 75220(0.46MPa) ℃（℉）
Linear coefficient of thermal expansionASTM D696/ISO 113590.32 mm/mm.℃
Physical propertiesTest ConditionTest MethodTest Result
Taber abraser1000g,CS-17ASTM D-10443.5%水｜- mg/1000次
Taber abraser1000g,CS-17ASTM D-1044无水｜8 mg/1000次
Shrinkage rateMD：1.00mm3%0.80-1.5 --
Shrinkage rateMD：3.00mm4%1.5-2.2 --
Water absorption rate23°C,24hr%1.2 --
Water absorption rateSaturation,23°C%8.0 --
densityASTM D792/ISO 11831.14
Water absorption rateASTM D570/ISO 621.2 %
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityASTM D-2573.5%水｜1012-1013 Ω.cm
Dissipation factor50HzASTM D-150无水｜0.06
Dissipation factor50HzASTM D-1503.5%水｜-
Compared to the Leakage Traceability Index (CTI)UL 746无水｜- V
Compared to the Leakage Traceability Index (CTI)UL 7463.5%水｜530 V
Dielectric constant50HzASTM D-150无水｜1.6
Dielectric constant50HzASTM D-1503.5%水｜-
Volume resistivityASTM D-257无水｜1014-1015 Ω.cm
Volume resistivityohms·cm1.0E+13-1.0E+14 1.0E+12到1.0E+13
Dielectric constant23°C,50Hz1.60 --
Dissipation factor23°C,50Hz0.060 --
Compared to the anti leakage trace indexCTIV --
Dielectric constantASTM D150/IEC 602503.3
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-Sale,23°C119
Rockwell hardnessR-Sale,80°C97 --
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.