ABS

ABS TR-551 LG CHEM KOREA

236

Unit Price:US$ 3,013 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Extrusion grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	3200 μm, Injection	ASTM D1003	90.0 %
turbidity	Injection	ASTM D1003	1.9 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C, 3.20 mm, Injection	ASTM D638	2650 Mpa
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	59.0 Mpa
elongation	Yield, 23°C, 3.20 mm, Injection	ASTM D638	> 5.0 %
elongation	elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	> 15 %
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	2850 Mpa
bending strength	23°C, 3.20 mm, Injection	ASTM D790	96.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Temperature at the rear of the barrel			190 to 210 °C
Temperature in the middle of the barrel			200 to 220 °C
Temperature at the front of the material cylinder			210 to 230 °C
Spray nozzle temperature			210 to 240 °C
Processing (melt) temperature			210 to 240 °C
Mold temperature			40 to 70 °C
Back pressure			29.4 to 58.8 Mpa
Screw speed			< 80 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	87.0 °C
Vicat softening temperature		ASTM D15257	95.0 °C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI		UL 746	50.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	8.0 g/10 min
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.40 - 0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	117

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS TR-551 LG CHEM KOREA

Material Description

Technical Data Sheet Compare

Technical Data Sheet