POM Ultraform® N2200G43 BASF GERMANY

271

Unit Price:US$ 5,670 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜High rigidity｜high strength｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Fiber grade｜Electrical field｜Electronic field｜Household appliances｜Household appliances｜Lighting fixtures｜Automotive sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.5 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	50 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	7200 Mpa
tensile strength	Break	ISO 527-2	115 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
Tensile creep modulus	1000hr	ISO 899-1	4500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	161 °C
Melting temperature		ISO 11357-3	168 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	5E-05 cm/cm/°C
Maximum operating temperature	短周期操作		110 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.54 g/cm³
Apparent density			0.85 g/cm³
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	4.00 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.3 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.0 %
Water absorption rate	Saturation,23°C	ISO 62	0.90 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	1E+14 ohms·cm
Dielectric strength		IEC 60243-1	85 KV/mm
Relative permittivity	1MHz	IEC 60250	4.10
Dissipation factor	1MHz	IEC 60250	7E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	164 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
Automotive Materials	>1.00mm	FMVSS302	Passed
ISOType		ISO 9988-1	POM-K.M-GNR.02-003.GF20

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM Ultraform® N2200G43 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet