PBT Ultradur® B4040G6 HRBK BASF GERMANY

234

Unit Price:US$ 5,046 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
15MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Automotive External Parts｜Shell｜printed circuit board｜Application in the automotive field｜Industrial components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	48 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level	1.6mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	10500 Mpa
tensile strength	Break	ISO 527-2	140 Mpa
Tensile strain	Break	ISO 527-2	2.1 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Melting temperature		ISO 11357-3	223 °C
Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	2.5E-5到3.5E-5 cm/cm/°C
Maximum operating temperature	短周期操作		210 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	free,transverse		0.88 %
Apparent density			0.70to0.80 g/cm³
Melt Volume Flow Rate (MVR)	275°C/2.16kg	ISO 1133	33.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.31 %
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
Stickiness		ISO 307	85.0 cm³/g
Shrinkage rate	free,longitudinal		0.14 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+16 ohms·cm
Relative permittivity	100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.80
Dissipation factor	100Hz	IEC 60250	1.6E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.017
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Ultradur® B4040G6 HRBK BASF GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet