PBT

PBT VALOX™ 310-1001 SABIC INNOVATIVE US

240

Unit Price:US$ 3,286 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Glass fiber reinforced
Application Areas:Electrical applications｜Automotive Applications｜currency
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C6	ASTM D3029	40.7 J
Dart impact	Dart impact	23°C	ASTM D3029	40.7 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	300 %
tensile strength	Break	ASTM D638	51.7 Mpa
tensile strength	tensile strength	Yield	ASTM D638	51.7 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	82.7 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	82.7 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2340 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	154 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	54.4 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.4E-04 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI Str		UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.080 %
Shrinkage rate	TD：--3	Internal Method	1.6-2.4 %
	Shrinkage rate	TD：--2	Internal Method	1.0-1.7 %
		Shrinkage rate	MD：--3	Internal Method	1.5-2.3 %
		Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.90-1.6 %
Specific volume		ASTM D792	0.770 cm³/g
Melt viscosity		Internal Method	600 Pa·s

Electrical performance	Test Condition	Test Method	Test Result
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Arc resistance		ASTM D495	PLC 5
Dissipation factor	1MHz	ASTM D150	0.020
Dissipation factor	Dissipation factor	100Hz	ASTM D150	2E-03
Dielectric constant	1MHz	ASTM D150	3.10
Dielectric constant	Dielectric constant	100Hz	ASTM D150	3.30
Volume resistivity		ASTM D257	>4.0E+16 ohms·cm
Dielectric strength	1.60mm,inAir	ASTM D149	23 KV/mm
	Dielectric strength	1.60mm,in Oil	ASTM D149	23 KV/mm
		Dielectric strength	3.20mm,inAir	ASTM D149	16 KV/mm
		Dielectric strength	Dielectric strength	3.20mm,in Oil	ASTM D149	16 KV/mm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	117

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.