POM Delrin® 527UV GY DUPONT USA

94
  • Unit Price:US$ 2,296 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA8.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU260 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU260 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A8.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A8.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379521 mm/min
UL flame retardant rating0.8mmUL 94HB
UL flame retardant rating0.8mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
AtomizationF-value(refraction)4ISO 645290 %
AtomizationG-value(condensate)ISO 64522E-04 g
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainYieldISO 527-217 %
Nominal tensile fracture strainISO 527-230 %
Bending modulusISO 1783000 Mpa
bending strengthISO 17877.0 Mpa
Poisson's ratioISO 5270.37
Tensile modulusISO 527-23100 Mpa
tensile strengthYieldISO 527-270.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
AnnealingTemperature160 °C
AnnealingTime-Optional30.0 min/mm
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B163 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A95.0 °C
Vicat softening temperature--ISO 306/A50174 °C
Vicat softening temperature--ISO 306/B50160 °C
Melting temperatureISO 11357-3178 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21.2E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
densityISO 11831.42 g/cm³
melt mass-flow rate190°C/2.16kgISO 113315 g/10min
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 113313.0 cm3/10min
Shrinkage rateTDISO 294-41.9 %
Shrinkage rateMDISO 294-42.0 %
Water absorption rate23°C,24hrISO 620.50 %
Water absorption rateSaturation,23°C,2.00mmISO 621.2 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.20 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 600932E+13 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Relative permittivity100HzIEC 602503.80
Relative permittivity1MHzIEC 602503.80
Dissipation factor100HzIEC 602502.1E-03
Dissipation factor1MHzIEC 602505.6E-03
Compared to the anti leakage trace indexIEC 60112PLC 0
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessM-SaleISO 2039-292
Rockwell hardnessR-SaleISO 2039-2120
Supplementary InformationTest ConditionTest MethodTest Result
EmissionVDA275<8.00 mg/kg
EmissionofOrganicCompoundsVDA27716.0 µgC/g
OdorVDA2706.00
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.