PBT Toraycon® 1494X02 TORAY JAPAN

246

Unit Price:US$ 3,331 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
11MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Flame retardant grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			非增强阻燃等级.V-0

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-0 1.50mm
	UL flame retardant rating		UL -94	V-0 3.00mm
		UL flame retardant rating		UL -94	V-0 0.38mm
		UL flame retardant rating	UL flame retardant rating		UL -94	V-0 0.71mm

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	23℃·24hr	ASTM D-570	0.08 %

mechanical properties	Test Condition	Test Method	Test Result
compressive strength	23℃	ASTM D-695	930 kg/cm
Elongation at Break	23℃	ASTM D-638	20 %
Rockwell hardness		ASTM D-785	119
Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D-256	120 kg·cm/cm
	Impact strength of cantilever beam gap	Unnotched，-40℃	ASTM D-256	50 kg·cm/cm
		Impact strength of cantilever beam gap	Notched，23℃	ASTM D-256	3.5 kg·cm/cm
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Notched，-40℃	ASTM D-256	3.0 kg·cm/cm
tensile strength	23℃	ASTM D-638	620 kg/cm
bending strength	23℃	ASTM D-790	940 kg/cm
Bending modulus	23℃	ASTM D-790	28 kg/cm
tensile strength	23°C	ISO 527-2	64.0 Mpa
Elongation at Break	23°C	ISO 527-2	8.0 %
Tensile modulus	23°C	ISO 527-2	3000 Mpa
bending strength	23°C	ISO 178	105 Mpa
Bending modulus	23°C	ISO 178	2900 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	66 kJ/m²
Impact strength of cantilever beam gap		ASTM D256/ISO 179	30 kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	20 kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	90 kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	35 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	20 %
tensile strength		ASTM D638/ISO 527	65 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M86
Bending modulus		ASTM D790/ISO 178	2800 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	95 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D-696	9.0 cm/cm℃×10
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	136 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	64.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Combustibility (rate)		UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	9.0x10^-5 mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Hot deformation temperature	4.6kg/cm	ASTM D-648	165 °C
Hot deformation temperature	Hot deformation temperature	18.6kg/cm	ASTM D-648	60 °C
Friction coefficient	金属	ASTM D-1894	0.14
Friction coefficient	Friction coefficient	本身	ASTM D-1894	0.18
Taber abraser	1.000g·CS-17轮	ASTM D-1044	13 毫克/1.000m
Shrinkage rate	80×80×3板材		1.5-2.0 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	2.0 %
Water absorption rate	(23°C,24hr)	ISO 62	0.080 %
Shrinkage rate	MD	ISO 294-4	1.5 %
density		ASTM D792/ISO 1183	1.43
Water absorption rate		ASTM D570/ISO 62	0.08 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	短时·23℃·1/8时	ASTM D-149	17 KV/mm
Volume resistivity		ASTM D-257	1.0 cm×10
Arc resistance		ASTM D-495	70 秒
Volume resistivity		IEC 60093	2E+16 Ω.cm
Dielectric strength		IEC 60243-1	26 KV/mm
Dielectric constant	23°C	IEC 60250	3.40 1MHz
Dissipation factor	23°C	IEC 60250	0.020 1MHz
Dissipation factor	Dissipation factor	耐电弧性	IEC 61621	70.0 S
Dielectric constant		ASTM D150/IEC 60250	3.4
Volume resistivity		ASTM D257/IEC 60093	1.0x10^14 Ω.cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	82 M（Scale）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Toraycon® 1494X02 TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet