PBT CELANEX® 3201 CELANESE USA

234

Unit Price:US$ 4,212 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High toughness｜Hydrolysis resistance｜Thermal stability｜Weather resistance｜UV resistance｜Filler: Glass fiber reinforced material｜15% filler by weight
Application Areas:Electrical applications｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	7.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.5 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	--	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.9mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	6000 Mpa
tensile strength	Break,23°C	ASTM D638	93.1 Mpa
tensile strength	tensile strength	Break	ISO 527-2/1A/5	100 Mpa
elongation	Break,23°C	ASTM D638	3.0 %
Tensile strain	Break	ISO 527-2/1A/5	3.5 %
Bending modulus	23°C	ISO 178	5600 Mpa
bending strength	23°C	ISO 178	160 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	213 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	218 °C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	192 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	195 °C
Glass transition temperature		ISO 11357-2	60.0 °C
Vicat softening temperature		ISO 306/B50	220 °C
Melting temperature		ASTM D3418	225 °C
Melting temperature	Melting temperature		ISO 11357-3	225 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	3.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.41 g/cm³
density	density		ISO 1183	1.42 g/cm³
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	17.0 cm3/10min
Shrinkage rate	MD	ASTM D955	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1E+15 ohms·cm
Dielectric strength		ASTM D149	18 KV/mm
Dielectric constant	1kHz	ASTM D150	3.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT CELANEX® 3201 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet