Material Description

Material Properties:Middle flow｜Biocompatibility｜Steam sterilization
Application Areas:Medical devices｜Medical and nursing supplies
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0 kJ/m²
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	3.20mm	ASTM D256	1900 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	28.0 J
Dart impact	Dart impact	23°C	ASTM D3029	23.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.71mm	UL 94	V-2
	UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTM D638	7.0 %
Tensile strain	Yield	ISO 527-2/5	6.0 %
elongation	Break	ASTM D638	70 %
Tensile strain	Break	ISO 527-2/5	60 %
Bending modulus	100mmSpan4	ASTM D790	3720 Mpa
	Bending modulus	50.0mmSpan5	ASTM D790	3420 Mpa
	Bending modulus	Bending modulus		ISO 178	3300 Mpa
bending strength		ISO 178	140 Mpa
	bending strength	Yield,50.0mmSpan5	ASTM D790	174 Mpa
	bending strength	bending strength	Yield,100mmSpan4	ASTM D790	165 Mpa
Tensile modulus		ASTM D638	3720 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3500 Mpa
tensile strength	Yield	ASTM D638	110 Mpa
	tensile strength	Yield	ISO 527-2/5	110 Mpa
	tensile strength	tensile strength	Break	ASTM D638	85.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B50	200 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	205 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	5.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	5.5E-05 cm/cm/°C
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	170 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	199 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	210 °C
Vicat softening temperature		ASTM D152511	219 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6kg	ASTM D1238	16 g/10min
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.65 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 2
Hot wire ignition	HWI	UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ HU1110 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet