PC PANLITE® K-1300Y TEIJIN JAPAN

323

Unit Price:US$ 3,521 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
75MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent
Application Areas:transparent｜Translucent accessories｜film｜sheet｜Cleaning Compound
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Transmittance rate		ASTM D1003/ISO 13468	88 %
Refractive index		ASTM D542/ISO 489	1.585
Transmittance rate	3mm厚	ASTM D1003	88 %
Refractive index		ASTM D542	1.585
transmissivity	3000μm	ASTM D1003	88.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.38mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	89 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	- %
Tensile modulus		ASTM D638/ISO 527	2400 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	6 %
Bending modulus		ASTM D790/ISO 178	2200 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	90 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	>50 %
Tensile modulus		ISO 527-2/1	2350 Mpa
tensile strength	Yield	ISO 527-2/50	60.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Nominal tensile fracture strain		ISO 527-2/50	>50 %
Bending modulus		ISO 178	2200 Mpa
bending strength		ISO 178	90.0 Mpa
Tensile modulus		ISO 527-1	2350 Mpa
Tensile stress		ISO 527-1	60 Mpa
elongation at yield		ISO 527-1	6 %
elongation	Break	ISO 527-1	＞50 %
Bending modulus		ISO 178	2200 Mpa
Impact strength of cantilever beam gap	没Notched	ISO 179	NB KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	带Notched	ISO 179	89 KJ/m

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648/ISO 75	145 ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	151 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.7 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	132 °C
Vicat softening temperature		ISO 306/B50	151 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
RTI Str	1.5mm	UL 746	125 °C
Hot deformation temperature	1.80MPa	ISO 75-1	132 °C
Vicat softening temperature		ISO 306	151 °C
Linear coefficient of thermal expansion		ISO 11359-2	0.7
UL flame retardant rating		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1200
Shrinkage rate		ASTM D955	0.5-0.7 %
Water absorption rate		ASTM D570/ISO 62	0.2 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	2.80 cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Water absorption rate	23°C,24hr	ISO 62	0.20 %
Water absorption rate	Water absorption rate	23℃,24hrs	ISO 62	0.2 %
Shrinkage rate			0.5-0.7 %
Melt Volume Flow Rate (MVR)		ISO 1133	2.5 CM

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257/IEC 60093	>1×10 15 Ω
Dielectric constant		ASTM D150/IEC 60250	3
Dielectric constant	Dielectric constant		ASTM D150/IEC 60250	3.1
Arc resistance		ASTM D495/IEC 60112	30
Volume resistivity		ASTM D257/IEC 60093	>1×10 13 Ω.cm
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03
Dielectric constant	100HZ	IEC 60250	3.1
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3
Dielectric loss	100HZ，Tangent	IEC 60250	10
Dielectric loss	Dielectric loss	1MHZ，Tangent	IEC 60250	90
Volume resistivity		IEC 60093	＞1×10 Ω.m
Surface resistivity		IEC 60093	＞1×10 Ω
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC PANLITE® K-1300Y TEIJIN JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet