PPO

PPO NORYL™ PX1112-701 SABIC INNOVATIVE US

206

Unit Price:US$ 4,109 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Low Specific Gravity
Application Areas:Automotive body panels｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	17 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	17 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2100 Mpa
tensile strength	Yield	ISO 527-2/50	40.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	40.0 Mpa
Tensile strain	Yield	ISO 527-2/50	3.0 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	30 %
Bending modulus		ISO 178	1900 Mpa
bending strength		ISO 178	70.0 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	65.0 mg

injection	Test Condition	Test Method	Test Result
drying temperature			100 to 120 °C
drying time			2.0 to 3.0 hr
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			240 to 260 °C
Temperature in the middle of the barrel			260 to 280 °C
Temperature at the front of the material cylinder			280 to 300 °C
Spray nozzle temperature			260 to 280 °C
Processing (melt) temperature			280 to 300 °C
Mold temperature			80 to 120 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	120 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	105 °C
Vicat softening temperature	--	ISO 306/A50	130 °C
	Vicat softening temperature	--	ISO 306/B50	120 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	125 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.060 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Relative permittivity	50 Hz	IEC 60250	2.70
	Relative permittivity	60 Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.60
Dissipation factor	50 Hz	IEC 60250	4.0E-4
	Dissipation factor	60 Hz	IEC 60250	4.0E-4
	Dissipation factor	Dissipation factor	1 MHz	IEC 60250	1.0E-3

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	80.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ PX1112-701 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet