Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Electrical applications｜Lighting applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	30 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	240 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	470 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	20 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	30 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	68.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	83.0 Mpa
Bending modulus		ISO 178	2170 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2050 Mpa
Tensile strain	Break	ISO 527-2/5	74 %
elongation	Break	ASTM D638	56 %
Tensile strain	Yield	ISO 527-2/5	6.0 %
elongation	Yield	ASTM D638	5.0 %
tensile strength	Break	ISO 527-2/5	44.0 Mpa
	tensile strength	Break	ASTM D638	47.0 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/5	50.0 Mpa
Tensile modulus		ASTM D638	2240 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2040 Mpa
tensile strength	Yield	ASTM D638	54.0 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	90.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	139 °C
	Vicat softening temperature	--	ISO 306/B50	137 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D152510	136 °C
Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTM D648	115 °C
	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	115 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	124 °C
			Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	131 °C
				Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
				Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	130 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	22.0 cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	24 g/10min
density		ISO 1183	1.38 g/cm³
density	density		ASTM D792	1.38 g/cm³
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ BFL4000 WH3150 SABIC INNOVATIVE US

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet