plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
PPO

PPO NORYL™  GFN2 SABIC INNOVATIVE US

250
  • Unit Price:US$ 4,365 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    25MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details
  • Material Comparison:

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhance｜Glass fiber reinforced｜ Glass fiber reinforced
  • Application Areas:Household appliances｜Household appliances｜Fitness equipment｜Automotive interior parts
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/2C12 kJ/m²
Impact strength of cantilever beam gap-40°CASTM D25696 J/m
Impact strength of cantilever beam gap23°CASTM D256120 J/m
Impact strength of cantilever beam gap23°CISO 180/1A11 kJ/m²
Impact strength of cantilever beam gap23°CASTM D4812650 J/m
Dart impact23°C,TotalEnergyASTM D376322.6 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
Extreme Oxygen IndexASTM D286326 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6386200 Mpa
Tensile modulusISO 527-2/17070 Mpa
tensile strengthBreakASTM D63890.0 Mpa
tensile strengthBreakISO 527-2/597.3 Mpa
elongationBreakASTM D6382.6 %
Tensile strainBreakISO 527-2/52.5 %
Bending modulus50.0mmSpanASTM D7905800 Mpa
Bending modulusISO 1786540 Mpa
bending strengthISO 178167 Mpa
bending strengthYield,50.0mmSpanASTM D790160 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648135 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648138 °C
Hot deformation temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae137 °C
Vicat softening temperature--ISO 306/B50143 °C
Vicat softening temperature--ISO 306/B120146 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.9E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8318.3E-05 cm/cm/°C
RTI ElecUL 74690.0 °C
RTI ImpUL 74690.0 °C
RTI StrUL 74690.0 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648141 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648143 °C
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be143 °C
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D7921.20 g/cm³
melt mass-flow rate300°C/5.0kgASTM D12389.0 g/10min
Melt Volume Flow Rate (MVR)300°C/5.0kgISO 11338.10 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.20-0.50 %
Water absorption rate24hrASTM D5700.060 %
Outdoor applicabilityUL 746Cf1
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strength3.20mm,inOilASTM D14917 KV/mm
Dielectric constant50HzASTM D1502.86
Dielectric constant60HzASTM D1502.86
Dissipation factor50HzASTM D1508E-04
Dissipation factor60HzASTM D1508E-04
Arc resistanceASTM D495PLC7
High arc combustion indexHAIUL 746PLC 4
High voltage arc tracing rateHVTRUL 746PLC 4
Hot wire ignitionHWIUL 746PLC 4
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL-SaleASTM D785106
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.