ABS

ABS Toyolac® 100 TORAY MALAYSIA

380

Unit Price:US$ 1,859 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS Toyolac® 100 TORAY JAPAN

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance
Application Areas:Industrial machinery｜Fitness equipment
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	310 J/m
	Impact strength of cantilever beam gap	23°C,12.7mm	ASTM D256	290 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	0°C,12.7mm	ASTM D256	200 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	26 kJ/m²
Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	160 J/m
	Impact strength of cantilever beam gap	-30°C,12.7mm	ASTM D256	140 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	0°C,3.20mm	ASTM D256	230 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	63.0 Mpa
Tensile modulus		ISO 527-2/1	2100 Mpa
tensile strength	Yield	ASTM D638	41.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	44.0 Mpa
elongation	Break	ASTM D638	40 %
Tensile strain	Break	ISO 527-2/50	>10 %
Bending modulus		ASTM D790	1960 Mpa
bending strength		ASTM D790	63.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	85.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	91.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0 °C
Linear coefficient of thermal expansion	MD	ASTM D696	7.6E-05 cm/cm/°C
thermal conductivity		ASTMC177	0.15 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.04 g/cm³
density	density		ISO 1183	1.04 g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	15 g/10min
Shrinkage rate	MD	ASTM D955	0.40-0.60 %
Water absorption rate	23°C,24hr	ASTM D570	0.30 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	>1.0E+16 ohms
Volume resistivity	23°C	ASTM D257	>1.0E+16 ohms·cm
Dielectric strength		ASTM D149	24 KV/mm
Dielectric constant	1kHz	ASTM D150	3.10
Dissipation factor	1kHz	ASTM D150	6.5E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	105

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.