Material Description

Material Properties:Flame retardant｜High heat resistance
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	80 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	120 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	4340 Mpa
tensile strength	Yield	ISO 527-2/5	53.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	41.0 Mpa
Tensile strain	Yield	ISO 527-2/5	3.3 %
Tensile strain	Tensile strain	Break	ISO 527-2/5	14 %
Bending modulus		ISO 178	4110 Mpa
bending strength		ISO 178	92.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			110 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			50 to 80 %
Temperature at the rear of the barrel			245 to 265 °C
Temperature in the middle of the barrel			250 to 270 °C
Temperature at the front of the material cylinder			255 to 275 °C
Spray nozzle temperature			255 to 270 °C
Processing (melt) temperature			260 to 275 °C
Mold temperature			65 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			50 to 80 rpm
Exhaust hole depth			0.013 to 0.020 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	108 °C
Vicat softening temperature	--	ISO 306/B50	137 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140 °C
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	3.8E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	1.0E-4 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/5.0 kg	ASTM D1238	20 g/10 min
Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	17.0 cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Saturation, 23°C	ISO 62	0.42 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.14 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.