PC

PC Makrolon®  3208 COVESTRO THAILAND

290
  • Unit Price:US$ 6,288 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact resistance｜high molecular weight｜Drinking water contact
  • Application Areas:building materials｜Casters｜Transportation equipment
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity4000μmISO 13468-287.0 %
turbidity3000μmISO 14782<0.80 %
transmissivity1000μmISO 13468-289.0 %
transmissivity2000μmISO 13468-289.0 %
transmissivity3000μmISO 13468-288.0 %
Refractive indexISO 4891.587
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap23°C,Partial BreakISO 739175 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739120 kJ/m²
Charpy Notched Impact Strength-30°C,Complete BreakISO 739118 kJ/m²
Charpy Notched Impact Strength23°C,Partial BreakISO 739180 kJ/m²
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Multi axis Instrumented Peak Impact Force23°CISO 6603-25800 N
Multi axis Instrumented Peak Impact Force-30°CISO 6603-26700 N
Multi axis Instrumented Impact Energy23°CISO 6603-265.0 J
Multi axis Instrumented Impact Energy-30°CISO 6603-275.0 J
flammabilityTest ConditionTest MethodTest Result
FlashIgnitionTemperatureASTM D1929480 °C
SelfIgnitionASTM D1929550 °C
mechanical propertiesTest ConditionTest MethodTest Result
Bending strain23°CISO 1787.2 %
bending strength23°CISO 17895.0 Mpa
Tensile strainYield,23°CISO 527-2/506.3 %
Bending modulus23°CISO 1782350 Mpa
bending strength3.5%Strain,23°CISO 17872.0 Mpa
Tensile creep modulus1000hrISO 899-11900 Mpa
Tensile creep modulus1hrISO 899-12200 Mpa
Tensile strainBreak,23°CISO 527-2/50120 %
Nominal tensile fracture strain23°CISO 527-2/50>50 %
tensile strengthBreak,23°CISO 527-2/5075.0 Mpa
tensile strengthYield,23°CISO 527-2/5065.0 Mpa
Tensile modulus23°CISO 527-2/12350 Mpa
thermal performanceTest ConditionTest MethodTest Result
Ball Pressure Test141°CIEC 60695-10-2Pass
Vicat softening temperature--ISO 306/B120151 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A130 °C
Vicat softening temperature--ISO 306/B50150 °C
Glass transition temperatureISO 11357-2150 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B142 °C
thermal conductivity23°CISO 83020.20 W/m/K
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMDISO 25770.60-0.80 %
Water absorption rateSaturation,23°CISO 620.30 %
Shrinkage rateMD:2.00mm3ISO 294-40.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Shrinkage rateTD:2.00mm3ISO 294-40.75 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11335.00 cm3/10min
Shrinkage rateTDISO 25770.60-0.80 %
melt mass-flow rate300°C/1.2kgISO 11335.5 g/10min
density23°CISO 11831.20 g/cm³
Apparent densityISO 600.66 g/cm³
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1111 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.