Material Description

Material Properties:transparent｜High mobility｜High gloss｜High impact resistance｜Aging resistance
Application Areas:Thin walled products｜Electrical appliances｜switch｜Electronic field｜Electrical field｜Application in the automotive field｜light-emitting diode｜Car headlights
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ASTM D542	1.585
transmissivity	3000μm	ASTM D1003	88.0 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	62 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.9mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.40mm	UL 94	V-2
Burning wire flammability index	1.5mm	IEC 60695-2-12	825 °C
Burning wire flammability index	Burning wire flammability index	3.2mm	IEC 60695-2-12	875 °C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.2mm	IEC 60695-2-13	875 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	62.0 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Nominal tensile fracture strain		ISO 527-2/50	>50 %
Bending modulus		ISO 178	2400 Mpa
bending strength		ISO 178	95.0 Mpa
Tensile modulus		ISO 527-2/1	2400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
Vicat softening temperature		ISO 306/B50	144 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
RTI Str	1.5mm	UL 746	125 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.20 g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Water absorption rate	23°C,24hr	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC PANLITE® L-1225L BK JIAXING TEIJIN

Material Description

Technical Data Sheet Compare

Technical Data Sheet