POM

POM Delrin® SC690 NC010 DUPONT NETHERLANDS

322

Unit Price:US$ 5,068 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜High temperature resistance
Application Areas:household electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	200 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	200 kJ/m²

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ASTM D2863	23 %
Atomization	F-value (refraction)	ISO 6452	95 %
Atomization	Atomization	G-value (condensate)	ISO 6452	2.0E-4 g
Emission		VDA 275	< 8.00 mg/kg

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	3300 Mpa
tensile strength	Yield	ISO 527-2	71.0 Mpa
Tensile strain	Yield	ISO 527-2	12 %
Nominal tensile fracture strain		ISO 527-2	23 %
Tensile creep modulus	1 hr	ISO 899-1	2800 Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	1500 Mpa
Bending modulus		ISO 178	3000 Mpa
Poisson's ratio		ISO 527	0.37

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			210 to 220 °C
Melt Temperature, Optimum			215 °C
Mold temperature			80 to 100 °C
Mold Temperature, Optimum			90 °C
Maintain pressure			80.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			8.00 s/mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	162 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	94.0 °C
Vicat softening temperature		ISO 306/B50	160 °C
Melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ASTM E831	1.0E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.2E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.2E-4 cm/cm/°C
Annealing Time - Optional			30.0 min/mm
annealing temperature			160 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	25 g/10 min
Melt Volume Flow Rate (MVR)	190°C/2.16 kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	横向Flow	ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.9 %
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	1.4 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	0.30 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 62631-3-2	> 1.0E+15 ohms
Volume resistivity		IEC 62631-3-1	1.0E+12 ohms·m
Relative permittivity	100 Hz	IEC 62631-2-1	3.80
Relative permittivity	Relative permittivity	1 MHz	IEC 62631-2-1	3.80
Compared to the anti leakage trace index		IEC 60112	V
Hot wire ignition	0.750 mm	UL 746	sec

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale	ISO 2039-2	92
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM Delrin® SC690 NC010 DUPONT NETHERLANDS

Material Description

Technical Data Sheet Compare

Technical Data Sheet