POM

POM LNP™ LUBRICOMP™ K-2000 GY SABIC INNOVATIVE US

280

Unit Price:US$ 3,579 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
63MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜high strength｜Glass fiber reinforced
Application Areas:Automotive Applications
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.5 kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	6.41 J
Multi axis Instrumented Impact Energy		ISO 6603-2	0.820 J

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break	ASTM D638	32 %
Tensile strain	Yield	ISO 527-2	9.0 %
elongation	Yield	ASTM D638	9.3 %
tensile strength	Break	ISO 527-2	59.9 Mpa
	tensile strength	Break	ASTM D638	51.8 Mpa
		tensile strength	Yield	ISO 527-2	60.9 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	55.5 Mpa
Tensile modulus		ISO 527-2/1	2560 Mpa
Tensile modulus	Tensile modulus		ASTM D638	2070 Mpa
Wear factor	Washer	ASTM D3702Modified	10.0 10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.24
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.38
bending strength		ISO 178	65.6 Mpa
bending strength	bending strength		ASTM D790	84.1 Mpa
Bending modulus		ISO 178	2420 Mpa
Bending modulus	Bending modulus		ASTM D790	2430 Mpa
Tensile strain	Break	ISO 527-2	13 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	159 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	110 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	87.0 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr,50%RH	ASTM D570	0.33 %
Shrinkage rate	MD:24hr	ISO 294-4	2.2 %
	Shrinkage rate	TD:24hr	ISO 294-4	2.1 %
		Shrinkage rate	TD：24hr	ASTM D955	2.3 %
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	2.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM LNP™ LUBRICOMP™ K-2000 GY SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet