Material Description

Material Properties:Middle flow
Application Areas:Tool handle｜Home appliance components｜Automotive Interior Parts｜Electrical equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	480 J/m
Dart impact	23°C, Total Energy	ASTM D3763	12.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	5790 Mpa
tensile strength	Yield	ASTM D638	107 Mpa
tensile strength	tensile strength	Break	ASTM D638	107 Mpa
elongation	Yield	ASTM D638	3.0 %
elongation	elongation	Break	ASTM D638	3.0 %
Bending modulus	50.0 mm Span3	ASTM D790	5510 Mpa
Bending modulus	Bending modulus	100 mm Span4	ASTM D790	5100 Mpa
bending strength	Yield, 50.0 mm Span3	ASTM D790	172 Mpa
bending strength	bending strength	Break, 100 mm Span4	ASTM D790	172 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	210 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	212 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	205 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	207 °C
Vicat softening temperature		ASTM D15255	210 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	3.6E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	105 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	15 g/10 min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %

Electrical performance	Test Method	Test Result
Arc resistance	ASTM D495	PLC 5
Compared to the anti leakage trace index	UL 746	PLC 4
High arc combustion index	UL 746	PLC 4
High voltage arc tracing rate	UL 746	PLC 4
Hot wire ignition	UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.