PC/ABS

PC/ABS CYCOLOY™ LG9000-BK1001 SABIC INNOVATIVE NANSHA

224

Unit Price:US$ 3,155 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance
Application Areas:Automotive sector
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°, 无织构	ASTM D523	30

impact performance	Test Condition	Test Method	Test Result
Dart impact	-30°C, Total Energy	ASTM D3763	33.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	40.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	54.0 Mpa
elongation	Break	ASTM D638	75 %
Bending modulus	50.0 mm Span	ASTM D790	2300 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	84.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.040 %
Suggested injection volume			30 to 80 %
Temperature at the rear of the barrel			250 to 290 °C
Temperature in the middle of the barrel			255 to 295 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			275 to 300 °C
Processing (melt) temperature			275 to 300 °C
Mold temperature			60 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	123 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	129 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	107 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	110 °C
Vicat softening temperature		ASTM D15254	129 °C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.20 W/m/K
RTI Elec		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI		UL 746	60.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	17 g/10 min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.10 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.40 %

Electrical performance	Test Method	Test Result
Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	UL 746	PLC 0
Hot wire ignition	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.