PPO

PPO NORYL™ N1250 BK1066 SABIC INNOVATIVE SHANGHAI

375

Unit Price:US$ 3,930 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜High mobility｜Glass fiber reinforced
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	40.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.76 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5 mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2680 Mpa
tensile strength	Yield	ASTM D638	75.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	64.0 Mpa
elongation	Yield	ASTM D638	4.6 %
elongation	elongation	Break	ASTM D638	25 %
Bending modulus	50.0 mm Span	ASTM D790	2680 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	113 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			105 to 110 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			245 to 295 °C
Temperature in the middle of the barrel			255 to 300 °C
Temperature at the front of the material cylinder			265 to 305 °C
Spray nozzle temperature			275 to 305 °C
Processing (melt) temperature			275 to 305 °C
Mold temperature			70 to 100 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm
Exhaust hole depth			0.038 to 0.051 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	133 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	116 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	122 °C
Vicat softening temperature		ASTM D15255	137 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.1E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.8E-5 cm/cm/°C
RTI Elec		UL 746	110 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	115 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/5.0 kg	ASTM D1238	28 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

Electrical performance	Test Method	Test Result
Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	UL 746	PLC 0
High Voltage Arc Resistance Index (HVAR) (PLC)	UL 746	PLC 4
Hot wire ignition	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ N1250 BK1066 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet