PC/ABS

PC/ABS WONDERLOY® PC-510 TAIWAN CHIMEI

450

Unit Price:US$ 3,398 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
48MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Flame retardant｜heat-resisting
Application Areas:Electronic and electrical components
Color:--
Grade:Injection grade

Material Certification

MSDS

RoHS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180	45 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	45 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	590 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180	15 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	2.1mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ASTM D638	100 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	110 %
Bending modulus	23°C	ASTM D790	245 Mpa
Bending modulus	Bending modulus		ISO 178	2500 Mpa
bending strength	23°C	ASTM D790	78.5 Mpa
bending strength	bending strength		ISO 178	80.0 Mpa
tensile strength	Yield,23°C	ASTM D638	49.0 Mpa
	tensile strength	Yield	ISO 527-2/50	55.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	45.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	78.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	87.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	73.0 °C
Vicat softening temperature	--	ASTM D152510	94.0 °C
	Vicat softening temperature	--	ASTM D152511	85.0 °C
		Vicat softening temperature	--	ISO 306/A50	94.0 °C
		Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	85.0 °C

Physical properties	Test Condition	Test Method	Test Result
density	比重	ASTM D792	1.17 g/cm³
density	density	23°C	ISO 1183	1.17 g/cm³
melt mass-flow rate	260°C/2.16kg	ASTM D1238	20 g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16kg	ISO 1133	21.0 cm3/10min
Spiral flow length		Internal Method	45.0 CM
Shrinkage rate	MD	ASTM D955	0.40-0.60 %
Shrinkage rate	Shrinkage rate		ISO 2577	0.40-0.60 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	2.9E+17 ohms
Volume resistivity		IEC 60093	3.9E+19 ohms·cm
Dielectric constant	1MHz	IEC 60250	3.10

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ASTM D785	113
Rockwell hardness	Rockwell hardness	R-Sale,23°C	ISO 2039-2	113

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS WONDERLOY® PC-510 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet