PC/ABS

PC/ABS INFINO® WP-1041G Samsung Cheil South Korea

272

Unit Price:US$ 3,753 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Tool handle｜TV
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	35 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	45 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	47 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	1900 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	1900 Mpa
tensile strength	Yield	ASTM D638	49.0 Mpa
	tensile strength	Yield	ISO 527-2/50	47.0 Mpa
		tensile strength	Break	ASTM D638	39.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	41.0 Mpa
elongation	Break	ASTM D638	100 %
Tensile strain	Break	ISO 527-2/50	73 %
Bending modulus		ASTM D790	1900 Mpa
Bending modulus	Bending modulus		ISO 178	2000 Mpa
bending strength		ASTM D790	66.0 Mpa
bending strength	bending strength		ISO 178	70.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：40to100°C	ASTME831	8.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：40to100°C	ISO 11359-2	8.5E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	120 °C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	116 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	100 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	101 °C
Vicat softening temperature	--	ISO 306/B50	111to113 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	114 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：3.20mm	ASTM D955	0.40-0.70 %
	Shrinkage rate	TD:3.20mm	ISO 2577	0.40-0.70 %
	Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.40-0.70 %
melt mass-flow rate	250°C/10.0kg	ASTM D1238	31 g/10min
	melt mass-flow rate	250°C/2.16kg	ASTM D1238	3.0 g/10min
		melt mass-flow rate	250°C/10.0kg	ISO 1133	31 g/10min
		melt mass-flow rate	melt mass-flow rate	250°C/2.16kg	ISO 1133	3.0 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	105
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	107

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS INFINO® WP-1041G Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet