PC/PET

PC/PET XYLEX™  HX8300HP-1H9A002T SABIC INNOVATIVE US

393
  • Unit Price:US$ 3,530 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    62MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜High heat resistance
  • Application Areas:Automotive Applications｜Electronic and electrical accessories
  • Color:--
  • Grade:--

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
turbidity2540 μmASTM D1003< 2.0 %
transmissivity2540 μmASTM D100388.0 %
Refractive indexISO 4891.539
impact performanceTest ConditionTest MethodTest Result
Dart impact23°C, Total EnergyASTM D376395.0 J
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index1.0 mmIEC 60695-2-12750 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6381520 Mpa
Tensile modulus--ISO 527-2/11600 Mpa
tensile strengthYield3ASTM D63847.0 Mpa
tensile strengthYieldISO 527-2/5055.0 Mpa
tensile strengthBreak3ASTM D63846.0 Mpa
tensile strengthBreakISO 527-2/5054.0 Mpa
elongationBreakISO 527-2/50> 200 %
Bending modulus50.0 mm Span4ASTM D7901680 Mpa
Bending modulus--5ISO 1781700 Mpa
bending strength--5,6ISO 17878.0 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79071.0 Mpa
elongationBreak3ASTM D638150 %
elongationYieldISO 527-2/505.0 %
elongationYield3ASTM D6385.0 %
injectionTest ConditionTest MethodTest Result
Spray nozzle temperature245 to 265 °C
Temperature at the front of the material cylinder245 to 265 °C
Temperature in the middle of the barrel240 to 260 °C
Temperature at the rear of the barrel240 to 250 °C
Suggested injection volume40 to 80 %
Suggested maximum moisture content0.020 %
drying time3.0 to 5.0 hr
drying temperature65 to 75 °C
Processing (melt) temperature245 to 265 °C
Mold temperature45 to 60 °C
Back pressure0.200 to 0.500 Mpa
Screw speed20 to 100 rpm
Exhaust hole depth0.013 to 0.020 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64875.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Ae80.0 °C
Vicat softening temperature--ASTM D15251096.0 °C
Linear coefficient of thermal expansionFlow : 23 to 60°CISO 11359-29.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8311.1E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-21.1E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 60°CISO 11359-29.0E-5 cm/cm/°C
thermal conductivityISO 83020.23 W/m/K
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8311.1E-4 cm/cm/°C
Ball Pressure Test85°CIEC 60695-10-2通过
Vicat softening temperature--ISO 306/B5092.0 °C
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D64879.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate265°C/2.16 kgASTM D123815 g/10 min
Melt Volume Flow Rate (MVR)265°C/2.16 kgISO 113315.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.50 - 0.80 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.60 %
Water absorption rateSaturation, 23°CISO 620.49 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexUL 746PLC 0
Volume resistivityASTM D257> 1.0E+15 ohms·cm
Surface resistivityASTM D257> 1.0E+15 ohms
hardnessTest ConditionTest MethodTest Result
Shore hardnessShore D, 10 SecASTM D224073
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.