PC LEXAN™ ML6413 WH7D174 SABIC INNOVATIVE NANSHA

220

Unit Price:US$ 4,284 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High optical masking
Application Areas:Lighting applications｜Electronic and Electrical Applications｜Plastic bag
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	72.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6 mm	UL 94	V-0
	UL flame retardant rating	2.0 mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.6 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--1	ASTM D638	2500 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350 Mpa
tensile strength	Yield2	ASTM D638	58.0 Mpa
	tensile strength	Yield	ISO 527-2/50	62.0 Mpa
		tensile strength	Break2	ASTM D638	55.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	58.0 Mpa
elongation	Yield2	ASTM D638	5.0 %
	elongation	Yield	ISO 527-2/50	5.0 %
		elongation	Break2	ASTM D638	100 %
		elongation	elongation	Break	ISO 527-2/50	100 %
Bending modulus	50.0 mm Span3	ASTM D790	2250 Mpa
Bending modulus	Bending modulus	--4	ISO 178	2350 Mpa
bending strength	--4,5	ISO 178	90.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span3	ASTM D790	85.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			90 to 100 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			230 to 260 °C
Temperature in the middle of the barrel			250 to 290 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			250 to 290 °C
Processing (melt) temperature			270 to 300 °C
Mold temperature			60 to 90 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span7	ISO 75-2/Be	125 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	118 °C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span7	ISO 75-2/Ae	115 °C
Vicat softening temperature	--	ASTM D152512	134 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	135 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.9E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
RTI Elec		UL 746	100 °C
RTI Imp		UL 746	100 °C
RTI		UL 746	100 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	24 g/10 min
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	20.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.80 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

Electrical performance	Test Method	Test Result
Volume resistivity	ASTM D257	> 1.0E+15 ohms·cm
Compared to the anti leakage trace index	UL 746	PLC 2
Hot wire ignition	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ ML6413 WH7D174 SABIC INNOVATIVE NANSHA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet