PC LEXAN™  BFL4000U WH3150 SABIC INNOVATIVE NANSHA

242
  • Unit Price:US$ 4,047 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    12MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:UV resistance｜Flame retardant
  • Application Areas:Lighting applications
  • Color:--
  • Grade:Light diffusion level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/1eA30 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D256240 J/m
Impact strength of cantilever beam gap23°CASTM D256470 J/m
Impact strength of cantilever beam gap-30°CISO 180/1A20 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A30 kJ/m²
Dart impact23°C,TotalEnergyASTM D376368.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldISO 527-2/550.0 Mpa
tensile strengthBreakASTM D63847.0 Mpa
tensile strengthBreakISO 527-2/544.0 Mpa
elongationYieldASTM D6385.0 %
Tensile strainYieldISO 527-2/56.0 %
elongationBreakASTM D63856 %
Tensile strainBreakISO 527-2/574 %
Bending modulus50.0mmSpanASTM D7902050 Mpa
Bending modulusISO 1782170 Mpa
bending strengthISO 17883.0 Mpa
Tensile modulusASTM D6382240 Mpa
Tensile modulusISO 527-2/12040 Mpa
tensile strengthYieldASTM D63854.0 Mpa
bending strengthYield,50.0mmSpanASTM D79090.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648124 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af115 °C
Hot deformation temperature1.8MPa,Annealed,3.20mmASTM D648115 °C
Vicat softening temperatureASTM D152510136 °C
Vicat softening temperature--ISO 306/B50137 °C
Vicat softening temperature--ISO 306/B120139 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27.5E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648131 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648134 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf130 °C
Physical propertiesTest ConditionTest MethodTest Result
densityASTM D7921.38 g/cm³
densityISO 11831.38 g/cm³
melt mass-flow rate300°C/1.2kgASTM D123824 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113322.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.