ABS/PC

ABS/PC CYCOLAC™ DL200H-BK4051 SABIC INNOVATIVE NANSHA

144

Unit Price:US$ 3,294 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High heat resistance｜Hydrolysis resistance
Application Areas:Automotive components｜Electronic and electrical components
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	56 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	30 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	21 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2330 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2350 Mpa
tensile strength	Yield	ASTM D638	47.0 Mpa
	tensile strength	Yield	ISO 527-2/50	49.0 Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	40.0 Mpa
Tensile strain	Yield	ISO 527-2/50	3.9 %
elongation	Break	ASTM D638	70 %
Tensile strain	Break	ISO 527-2/50	75 %
Bending modulus	50.0mmSpan	ASTM D790	2200 Mpa
Bending modulus	Bending modulus		ISO 178	2100 Mpa
bending strength		ISO 178	75.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	77.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	118 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	120 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	96.0 °C
			Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	101 °C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	96.0 °C
Vicat softening temperature	--	ISO 306/B50	112 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	114 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0kg	ASTM D1238	25 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	9.0 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS/PC CYCOLAC™ DL200H-BK4051 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet