PC LEXAN™ HF1110-111 SABIC INNOVATIVE NANSHA

311

Unit Price:US$ 2,504 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
48MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High temperature resistance｜transparent
Application Areas:Electronic and electrical accessories｜Automotive components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
turbidity	2540 μm	ASTM D1003	1.0 %
transmissivity	2540 μm	ASTM D1003	88.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D1822	378 kJ/m²
Dart impact	23°C, Energy at Peak	ASTM D3763	54.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.1 mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span	ASTM D790	93.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2300 Mpa
elongation	Break	ASTM D638	120 %
tensile strength	Break	ASTM D638	65.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	62.0 Mpa

injection	Test Condition	Test Method	Test Result
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
drying temperature			120 °C
Temperature at the rear of the barrel			250 to 270 °C
Temperature in the middle of the barrel			260 to 280 °C
Temperature at the front of the material cylinder			270 to 295 °C
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm
Spray nozzle temperature			265 to 290 °C
Processing (melt) temperature			270 to 295 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	130 °C
RTI Imp		UL 746	130 °C
RTI Elec		UL 746	130 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58 %
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35 %
	Water absorption rate	Water absorption rate	24 hr	ASTM D570	0.10 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	25 g/10 min

Electrical performance	Test Method	Test Result
Hot wire ignition	UL 746	PLC 2
High voltage arc tracing rate	UL 746	PLC 2
High arc combustion index	UL 746	PLC 1
Compared to the anti leakage trace index	UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ HF1110-111 SABIC INNOVATIVE NANSHA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet