PA12 LNP™ LUBRICOMP™  SCL-4536（SCP36） SABIC INNOVATIVE US

254
  • Unit Price:US$ 9,264 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    44.6MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:lubrication｜wear resistant｜Filler: Carbon fiber reinforced material｜30% filler by weight
  • Application Areas:Electrical appliances｜Plastic bag
  • Color:--
  • Grade:Conductive grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U34 kJ/m²
Dart impact23°C,TotalEnergyASTM D376310.0 J
Multi axis Instrumented Impact EnergyISO 6603-22.00 J
Impact strength of cantilever beam gap23°CISO 180/1A7.0 kJ/m²
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulus50.0mmSpanASTM D79016200 Mpa
Bending modulusISO 17816000 Mpa
bending strengthBreak,50.0mmSpanASTM D790178 Mpa
Friction coefficientDynamicASTM D3702Modified0.47
Friction coefficientStaticASTM D3702Modified0.33
Wear factorRingASTM D3702Modified0.00 10^-10in^5-min/ft-lb-hr
Wear factorWasherASTM D3702Modified14.0 10^-10in^5-min/ft-lb-hr
Tensile modulusISO 527-2/118200 Mpa
tensile strengthBreakASTM D6381.00 Mpa
tensile strengthBreakISO 527-2/5122 Mpa
elongationBreakASTM D6381.0 %
Tensile strainBreakISO 527-2/51.0 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648178 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf177 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648173 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af169 °C
Linear coefficient of thermal expansionMD：-30to30°CASTM D6963.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-30to30°CASTM D6964.1E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMD：24hrASTM D9550.10 %
Shrinkage rateTD：24hrASTM D9550.50 %
Water absorption rate24hr,50%RHASTM D5700.16 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.24 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.