PC/ABS

PC/ABS CYCOLOY™ CM6240-701 SABIC INNOVATIVE NANSHA

236

Unit Price:US$ 3,158 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12.6MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Low warpage
Application Areas:Electronic and electrical components｜Automotive components｜Plate
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	-30°C, Total Energy	ASTM D3763	35.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	56.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	4350 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	4460 Mpa
tensile strength	Yield3	ASTM D638	55.0 Mpa
	tensile strength	Yield	ISO 527-2/5	56.0 Mpa
		tensile strength	Break3	ASTM D638	40.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	29.0 Mpa
elongation	Yield3	ASTM D638	3.0 %
	elongation	Yield	ISO 527-2/5	3.0 %
		elongation	Break3	ASTM D638	35 %
		elongation	elongation	Break	ISO 527-2/5	25 %
Bending modulus	50.0 mm Span4	ASTM D790	4400 Mpa
Bending modulus	Bending modulus	--5	ISO 178	4510 Mpa
bending strength	--5,6	ISO 178	101 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	96.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.040 %
Temperature at the rear of the barrel			220 to 255 °C
Temperature in the middle of the barrel			230 to 275 °C
Temperature at the front of the material cylinder			255 to 285 °C
Spray nozzle temperature			255 to 285 °C
Processing (melt) temperature			255 to 285 °C
Mold temperature			70 to 95 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	90.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	86.0 °C
Vicat softening temperature	--	ASTM D15259	97.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	100 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	4.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	4.8E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.4E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.3E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	17 g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	Flow	Internal Method	0.33 %
	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.30 - 0.40 %
	Shrinkage rate	Shrinkage rate	Across FlowFlow	Internal Method	0.38 %
Water absorption rate	Saturation, 23°C	ISO 62	0.10 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.030 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLOY™ CM6240-701 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet