PBT

PBT NOVADURAN™ 5010N6-X3 MITSUBISHI ENGINEERING JAPAN

196

Unit Price:US$ 5,670 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Bottle cap｜Automotive Applications
Color:--
Grade:Halogen-free flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	120 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.71 mm	UL 94	V-0
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	2800 Mpa
tensile strength	Yield	ISO 527-2/50	57.0 Mpa
Tensile strain	Yield	ISO 527-2/50	4.3 %
Tensile strain	Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ISO 178	2500 Mpa
bending strength		ISO 178	90.0 Mpa

injection	Test Condition	Test Method	Test Result
Drying Temperature - Vacuum Drying Machine			120 °C
Drying time - vacuum dryer			5.0 to 8.0 hr
Temperature at the rear of the barrel			235 °C
Temperature in the middle of the barrel			240 °C
Temperature at the front of the material cylinder			250 °C
Spray nozzle temperature			245 °C
Mold temperature			60 to 80 °C
Injection pressure			20.0 to 150 Mpa
Injection speed			中等偏快
Screw speed			80 to 120 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Annealed	ISO 75-2/B	165 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Annealed	ISO 75-2/A	77.0 °C
Melting temperature		ISO 11357-3	224 °C
Linear coefficient of thermal expansion	Flow : -30 to 35°C	ISO 11359-2	8.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : -30 to 120°C	ISO 11359-2	1.2E-4 cm/cm/°C
		Linear coefficient of thermal expansion	Flow : 35 to 120°C	ISO 11359-2	1.4E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow : -30 to 35°C	ISO 11359-2	8.8E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Across Flow : -30 to 120°C	ISO 11359-2	1.2E-4 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 35 to 120°C	ISO 11359-2	1.5E-4 cm/cm/°C
RTI Elec	0.71 mm	UL 746	140 °C
RTI Imp	0.71 mm	UL 746	120 °C
RTI	0.71 mm	UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	250°C/2.16 kg	ISO 1133	20.0 cm3/10min
Shrinkage rate	横向Flow : 2.00 mm	Internal Method	1.8 %
Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	Internal Method	1.9 %
Water absorption rate	Saturation, 23°C	ISO 62	0.080 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1.0E+15 ohms
Volume resistivity		IEC 60093	1.0E+16 ohms·cm
Dielectric strength	1.00 mm	IEC 60243-1	21 KV/mm
Dielectric strength	Dielectric strength	2.00 mm	IEC 60243-1	18 KV/mm
Dielectric constant	1 MHz	IEC 60250	3.20
Dissipation factor	1 MHz	IEC 60250	0.020
Compared to the anti leakage trace index		UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT NOVADURAN™ 5010N6-X3 MITSUBISHI ENGINEERING JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet