Material Description

Material Properties:High rigidity｜Glass fiber reinforced
Application Areas:Engineering accessories｜Shell｜electrical machinery｜printed circuit board
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	26 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level	0.75mm	IEC 60695-11-10,-20	HB
Flammability level	Flammability level	1.6mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	3500 Mpa
tensile strength	Break	ISO 527-2	48.0 Mpa
Tensile strain	Break	ISO 527-2	6.0 %
Tensile creep modulus	1000hr	ISO 899-1	1300 Mpa
Bending modulus		ISO 178	3400 Mpa
bending strength		ISO 178	100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	170 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Melting temperature		ISO 11357-3	223 °C
Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	8.0E-5到9.0E-5 cm/cm/°C
specific heat			1150 J/kg/°C
thermal conductivity		DIN 52612	0.27 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Stickiness		ISO 307	115 cm³/g
Apparent density			0.70to0.80 g/cm³
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	16.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.9 %
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1MHz	IEC 60250	3.70
Dissipation factor	100Hz	IEC 60250	0.012
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.019
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 4
Surface resistivity		IEC 60093	1E+13 ohms
Volume resistivity		IEC 60093	1E+16 ohms·cm
Relative permittivity	100Hz	IEC 60250	4.00

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	150 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Ultradur® B 4300 K4 BASF GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet