PC/ABS

PC/ABS CYCOLAC™ C7230P 5MD018 SABIC INNOVATIVE US

176

Unit Price:US$ 4,113 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Aging resistance｜High mobility
Application Areas:Electronic and electrical accessories｜Casters｜Household appliances
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		80104; ISO 180/1A	5 kJ/m²
	Impact strength of cantilever beam gap			@Temperature -30.0
		Impact strength of cantilever beam gap		ASTM D256	0.55 J/cm
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	0.69 J/cm
Bending modulus		2 mm/min; ISO 178	4.58
Bending modulus	Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	4.53
bending strength		2 mm/min; ISO 178	99 Mpa
bending strength	bending strength	1.3 mm/min, 50 mm span	ASTM D790	98 Mpa
tensile strength	Type I, 50 mm/min，Yield	ASTM D638	58 Mpa
	tensile strength	Yield	ISO 178	55 Mpa
		tensile strength	Type I, 50 mm/min，Yield	ASTM D638	45 Mpa
		tensile strength	tensile strength	Yield	ISO 178	35 Mpa
Tensile modulus		1 mm/min; ISO 527	5.58
Tensile modulus	Tensile modulus		GB/T 15585-1995	5.2
elongation at yield	Type I, 50 mm/min	ASTM D638	4 %
elongation at yield	elongation at yield		ISO 178	3.8 %
Elongation at Break	Type I, 50 mm/min，Break	ASTM D638	32 %
Elongation at Break	Elongation at Break	Break	ISO 178	30 %
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5 J/cm²

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow	GB 1040	42 µm/m-°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	42 µm/m-°C
		Linear coefficient of thermal expansion	Across Flow	GB 1040	49 µm/m-°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	59 µm/m-°C
Hot deformation temperature	1.8 MPa	Flatw 80104 sp=64mm; ISO 75/Af	89
Hot deformation temperature	Hot deformation temperature	1.8 MPa	ASTMF1249	88
Vicat softening temperature		Rate B/50; ISO 306	107
	Vicat softening temperature		Rate B/50; ASTM D1525	108
	Vicat softening temperature	Vicat softening temperature		Equate	110
UL flame retardant rating		UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
Compound melt index			@Load 2.16 kg. Temperature 260
Compound melt index	Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C g/10 min
melt mass-flow rate		ASTM D1238	@Load 2.16 kg. Temperature 260
melt mass-flow rate	melt mass-flow rate		ASTM D1238	13
Shrinkage rate	Flow	SABIC method	0.0025 - 0.0035 cm/cm
Water absorption rate	Saturation	ISO 62	0.09 %
Water absorption rate	Water absorption rate		23°C / 50% RH; ISO 62	0.04 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS CYCOLAC™ C7230P 5MD018 SABIC INNOVATIVE US

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet