PA6 Ultramid® 6030G HS BK BASF GERMANY

220

Unit Price:US$ 3,958 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Oil resistant｜High impact resistance
Application Areas:Electrical enclosure｜film
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			可加工性良好热稳定良好的流动性
purpose			护罩支架家具

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	54 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	121
Tensile modulus	120°C	ISO 527-2	2730 Mpa
Tensile modulus	Tensile modulus	150°C	ISO 527-2	2890 Mpa
tensile strength	Break,-40°C	ISO 527-2	220 Mpa
	tensile strength	Break,23°C	ISO 527-2	155 Mpa
		tensile strength	Break,80°C	ISO 527-2	80.0 Mpa
			tensile strength	Break,120°C	ISO 527-2	65.0 Mpa
			tensile strength	tensile strength	Break,150°C	ISO 527-2	60.0 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
Bending modulus	23°C	ISO 178	8070 Mpa
bending strength	23°C	ISO 178	230 Mpa
Tensile modulus	-40°C	ISO 527-2	8740 Mpa
	Tensile modulus	23°C	ISO 527-2	9580 Mpa
	Tensile modulus	Tensile modulus	80°C	ISO 527-2	3820 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	219 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205 °C
Melting temperature		ISO 3146	220 °C
Linear coefficient of thermal expansion	MD		2.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		6.7E-05 cm/cm/°C
RTI Elec	0.8mm	UL 746	130 °C
	RTI Elec	1.5mm	UL 746	140 °C
	RTI Elec	RTI Elec	3.0mm	UL 746	140 °C
RTI Imp	0.8mm	UL 746	115 °C
	RTI Imp	1.5mm	UL 746	115 °C
	RTI Imp	RTI Imp	3.0mm	UL 746	120 °C
RTI Str	0.8mm	UL 746	130 °C
	RTI Str	1.5mm	UL 746	140 °C
	RTI Str	RTI Str	3.0mm	UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.36
Water absorption rate	23°C,24hr	ISO 62	1.1 %
	Water absorption rate	Saturation,23°C	ISO 62	6.7 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.9 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>1.0E+13 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® 6030G HS BK BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet