PC LNP™ THERMOCOMP™ LGN2000-731 SABIC INNOVATIVE NANSHA

179

Unit Price:US$ 3,438 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Flame retardant
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	14.2 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	400 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.50mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	81.0 Mpa
elongation	Break	ASTM D638	4.9 %
Bending modulus	50.0mmSpan	ASTM D790	5030 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	124 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	130 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	141 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	135 °C
Vicat softening temperature		ASTM D15255	144 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.3E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:-40to95°C	ASTME831	2.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	4.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to95°C	ASTME831	5.6E-05 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	300°C/1.2kg	ASTM D1238	21 g/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.15-0.25 %
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.25-0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ THERMOCOMP™ LGN2000-731 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet Compare

Technical Data Sheet