PEI ULTEM™ 2210EPR-1000 SABIC INNOVATIVE US

273

Unit Price:US$ 21,157 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High mobility
Application Areas:Automotive components｜Casters
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	14.9 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.41mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTM D638	3.0 %
elongation	elongation	Break	ASTM D638	3.0 %
Bending modulus	100mmSpan4	ASTM D790	6890 Mpa
Bending modulus	Bending modulus	50.0mmSpan5	ASTM D790	6890 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	207 Mpa
bending strength	bending strength	Break,100mmSpan	ASTM D790	207 Mpa
Tensile modulus		ASTM D638	6890 Mpa
tensile strength	Yield	ASTM D638	138 Mpa
tensile strength	tensile strength	Break	ASTM D638	138 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	214 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	206 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	209 °C
Vicat softening temperature		ASTM D15256	210 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
RTI Elec		UL 746	105 °C
RTI Imp		UL 746	105 °C
RTI Str		UL 746	105 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	211 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6kg	ASTM D1238	13 g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 1
Arc resistance		ASTM D495	PLC6

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 2210EPR-1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet