PA66

PA66 LNP™ THERMOCOMP™ RF00AS-BK1A817 SABIC INNOVATIVE NANSHA

223

Unit Price:US$ 4,184 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance
Application Areas:Electronic and Electrical Applications｜Chemical equipment｜sporting goods｜mechanical
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23℃ (73℉)	ASTM D256	149 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃ (73℉)80104	ISO 180/1A	13 kJ/m²
Suspended wall beam without notch impact strength	23℃ (73℉)80104	ISO 180/1U	65 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23℃ (73℉)	ASTM D4812	1585 J/m
Instrumented dart impact energy peak at 23 ℃ (73 ℉)	/	ASTM D3763	12 J
Multi axis impact	/	ISO 6603	3 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	/，Break	ASTM D638	197 Mpa
tensile strength	tensile strength	/，Break	ISO 527	194 Mpa
Elongation at Break	/	ASTM D638	2.4 %
Elongation at Break	Elongation at Break	/	ISO 527	2.4 %
bending strength	/	ASTM D790	312 Mpa
bending strength	bending strength	/	ISO 178	300 Mpa
Bending modulus	/	ASTM D790	12540 Mpa
Bending modulus	Bending modulus	/	ISO 178	14500 Mpa
Tensile modulus	50 mm/m	ASTM D638	17650 Mpa
Tensile modulus	Tensile modulus	1 mm/min	ISO 527	14000 Mpa

thermal properties	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	-40°C to，Flow	ASTM E831	27 E-6 °C
	Linear coefficient of thermal expansion	-40°C to，Flow	ISO 11359-2	28.1 E-6 °C
		Linear coefficient of thermal expansion	-40°C to，Across Flow	ASTM E831	43.2 E-6 °C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	-40°C to，Across Flow	ISO 11359-2	44.2 E-6 °C

combustion performance	Test Condition	Test Method	Test Result
UL flame retardant rating	HB	UL 94	1.5 mm

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	flow, 24 h	ASTM D 955	0.3 %
	Shrinkage rate	flow, 24 h	ISO 294	0.34 %
	Shrinkage rate	Shrinkage rate	xflow, 24，Across Flow	ASTM D 955	1.2 %
Water absorption rate	50% RH,	ASTM D 570	0.4 %
Water absorption rate	Water absorption rate	23°C / 50	ISO 62	0.74 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.