PA66

PA66 LNP™ THERMOCOMP™ RF-1004 BK8114 SABIC INNOVATIVE US

194

Unit Price:US$ 3,436 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High temperature resistance｜high strength｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Automotive components｜Electronic and electrical components
Color:--
Grade:Heat resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	2.49 J
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	11.4 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	56 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.6 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Wear factor	Washer	ASTM D3702Modified	80.0 10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.52
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.68
bending strength		ISO 178	242 Mpa
bending strength	bending strength		ASTM D790	231 Mpa
Bending modulus		ISO 178	7000 Mpa
Bending modulus	Bending modulus		ASTM D790	5860 Mpa
Tensile strain	Break	ISO 527-2	3.7 %
elongation	Break	ASTM D638	3.6 %
tensile strength	Break	ISO 527-2	160 Mpa
Tensile modulus		ASTM D638	7170 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	7300 Mpa
tensile strength	Break	ASTM D638	157 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	3.8E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	221 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	247 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	260 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD:24hr	ISO 294-4	0.47 %
	Shrinkage rate	TD:24hr	ISO 294-4	1.2 %
		Shrinkage rate	TD：24hr	ASTM D955	1.2 %
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.50 %
Water absorption rate	24hr,50%RH	ASTM D570	0.80 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 LNP™ THERMOCOMP™ RF-1004 BK8114 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet