plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
PC

PC LEXAN™  EXL9330-WH9A445 SABIC INNOVATIVE NANSHA

185
  • Unit Price:US$ 4,588 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    33MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Flame retardant｜Toughening｜UV resistance
  • Application Areas:food｜Thin walled products｜Casters
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Impact strength of cantilever beam gap23°C, 6.40 mmASTM D256640 J/m
Impact strength of cantilever beam gap23°C8Internal Method1100 J/m
Impact strength of cantilever beam gap23°CASTM D256800 J/m
Impact strength of cantilever beam gap-50°CASTM D256590 J/m
Impact strength of cantilever beam gap-30°CASTM D256680 J/m
Impact strength of cantilever beam gap23°C9ISO 180/1A70 kJ/m²
Impact strength of cantilever beam gap-30°C9ISO 180/1A55 kJ/m²
Impact strength of cantilever beam gap-30°C10ISO 180/4A65 kJ/m²
Impact strength of cantilever beam gap23°C10ISO 180/4A80 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376352.0 J
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
UL flame retardant rating3.0 mmUL 945VA
Extreme Oxygen IndexISO 4589-235 %
Hot filament ignition temperature1.0 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94V-0
mechanical propertiesTest ConditionTest MethodTest Result
elongationBreak3ASTM D638130 %
elongationBreakISO 527-2/50130 %
elongationYieldISO 527-2/506.0 %
elongationYield3ASTM D6386.0 %
tensile strengthBreakISO 527-2/5060.0 Mpa
tensile strengthBreak3ASTM D63861.0 Mpa
tensile strengthYieldISO 527-2/5055.0 Mpa
tensile strengthYield3ASTM D63858.0 Mpa
Tensile modulus--ISO 527-2/12100 Mpa
Tensile modulus--2ASTM D6382100 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79088.0 Mpa
bending strength--5,6ISO 17885.0 Mpa
Bending modulus--5ISO 1782200 Mpa
Bending modulus50.0 mm Span4ASTM D7902060 Mpa
injectionTest ConditionTest MethodTest Result
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Spray nozzle temperature290 to 310 °C
Temperature at the front of the material cylinder295 to 315 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the rear of the barrel215 to 295 °C
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
drying temperature120 °C
drying time3.0 to 4.0 hr
thermal performanceTest ConditionTest MethodTest Result
RTIUL 746120 °C
RTI ImpUL 746115 °C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.7E-5 cm/cm/°C
RTI ElecUL 746125 °C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.7E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-27.2E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8316.7E-5 cm/cm/°C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Vicat softening temperature--ISO 306/B50140 °C
Vicat softening temperature--ASTM D152512142 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 100 mm Span11ISO 75-2/Ae124 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648120 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648124 °C
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 100 mm Span11ISO 75-2/Be135 °C
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648134 °C
Physical propertiesTest ConditionTest MethodTest Result
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
density--ISO 11831.19 g/cm³
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
density--ASTM D7921.18 g/cm³
Outdoor applicabilityUL 746Cf1
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Water absorption rateSaturation, 23°CISO 620.35 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.80 %
Electrical performanceTest ConditionTest MethodTest Result
Hot wire ignitionUL 746PLC 1
Compared to the anti leakage trace indexIEC 60112PLC 3
High arc combustion indexUL 746PLC 0
Dissipation factor60 HzIEC 602501.0E-3
Compared to the anti leakage trace indexUL 746PLC 3
Dissipation factor50 HzIEC 602501.0E-3
Dissipation factor1 MHzASTM D1508.5E-3
Dissipation factor60 HzASTM D1502.4E-3
Dissipation factor50 HzASTM D1502.4E-3
Dielectric constant1 MHzIEC 602502.70
Dielectric constant60 HzIEC 602502.60
Dielectric constant50 HzIEC 602502.60
Dielectric constant1 MHzASTM D1502.90
Dielectric constant50 kHzASTM D1502.95
Dielectric constant60 HzASTM D1502.95
Dielectric strength3.20 mm, in OilIEC 60243-116 KV/mm
Dielectric strength3.20 mm, in OilASTM D14917 KV/mm
Surface resistivityIEC 60093> 1.0E+15 ohms
Volume resistivityIEC 60093> 1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestH 358/30ISO 2039-190.0 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.