PBT

PBT Toraycon® 1184G-15 TORAY JAPAN

274

Unit Price:US$ 3,516 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
69.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Glass fiber reinforced｜High toughness
Application Areas:Electrical components
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			增强阻燃等级.V-0.15%玻纤增强

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	50 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	5 %
tensile strength		ASTM D638/ISO 527	110 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M87
Bending modulus		ASTM D790/ISO 178	5600 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	150 kg/cm²(MPa)[Lb/in²]
tensile strength	23℃	ASTM D638	110 Mpa
elongation	23℃	ASTM D638	5 %
bending strength	23℃	ASTM D790	150 Mpa
Bending modulus	23℃	ASTM D790	5.6 GPa
Impact strength of cantilever beam gap	Notched，23℃	ASTM D256	60 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D256	50 KJ/m
Rockwell hardness		ASTM D785	87 M
Friction coefficient	对金属	ASTM D1894	0.15
Friction coefficient	Friction coefficient	对本身	ASTM D1894	0.20

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	200 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	5.3x10^-5 mm/mm.℃
Hot deformation temperature	0.45MPa	ASTM D648	215 °C
Hot deformation temperature	Hot deformation temperature	1.82Mpa	ASTM D648	200 °C
Linear coefficient of thermal expansion		ASTM D696	5.3
UL flame retardant rating		UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.56
Water absorption rate		ASTM D570/ISO 62	0.07 %
Water absorption rate	Water absorption rate	23℃,24hr	ASTM D570	0.07 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant		ASTM D150/IEC 60250	3.8
Volume resistivity		ASTM D257/IEC 60093	3.0x10^14 Ω.cm
Volume resistivity	Volume resistivity		ASTM D257	3.0
Dielectric strength		ASTM D149	25 MV/m
Dielectric constant	50Hz	ASTM D150	3.6
Dielectric constant	Dielectric constant	10	ASTM D150	3.8
Dielectric loss	50Hz，Tangent	ASTM D150	0.002
Dielectric loss	Dielectric loss	10，Tangent	ASTM D150	0.02
Arc resistance		ASTM D495	133 S

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Toraycon® 1184G-15 TORAY JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet