PC/PET

PC/PET XYLEX™ X7509HP SABIC INNOVATIVE US

342

Unit Price:US$ 3,713 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
62MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance
Application Areas:Electronic and electrical accessories
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	77.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2150 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2300 Mpa
bending strength		ISO 178	92.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	95.0 Mpa
tensile strength	Yield	ASTM D638	60.0 Mpa
	tensile strength	Yield	ISO 527-2/50	60.0 Mpa
		tensile strength	Break	ASTM D638	63.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	62.0 Mpa
elongation	Yield	ASTM D638	6.3 %
Tensile strain	Yield	ISO 527-2/50	5.8 %
elongation	Break	ASTM D638	140 %
Tensile strain	Break	ISO 527-2/50	130 %
Bending modulus	50.0mmSpan	ASTM D790	2300 Mpa
Bending modulus	Bending modulus		ISO 178	2260 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to60°C	ISO 11359-2	9E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	106 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	108 °C
Vicat softening temperature		ASTM D152511	126 °C
	Vicat softening temperature	--	ISO 306/B50	125 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	126 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	9E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	6.8E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	119 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	106 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/2.16kg	ASTM D1238	12 g/10min
Melt Volume Flow Rate (MVR)	265°C/2.16kg	ISO 1133	11.5 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.40-0.60 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Saturation,23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.050 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PET XYLEX™ X7509HP SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet