PBT

PBT DURANEX® 3300 JAPAN POLYPLASTIC

352

Unit Price:US$ 3,546 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Automotive sector
Color:--
Grade:Enhanced level

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	220 Mpa
tensile strength		ISO 527-2	140 Mpa
Tensile strain	Break	ISO 527-2	2.2 %
Bending modulus		ISO 178	9030 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	93 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	2.5 %
tensile strength		ASTM D638/ISO 527	132 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	9120 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	210 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	Notched侧	ASTM D-256	93 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	反Notched侧	ASTM D-256	530 J/m
elongation		ASTM D-638	2.5 %
tensile strength		ASTM D-638	132 Mpa
bending strength		ASTM D-790	210 Mpa
Bending modulus		ASTM D-790	9120 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	213 °C
Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	9E-05 cm/cm/°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	213 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2-7 mm/mm.℃
Linear expansion coefficient (room temperature)			2-7
Hot deformation temperature	1.82MPa	ASTM D-648	213 °C
UL flame retardant rating		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.10 %
density		ASTM D792/ISO 1183	1.53

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	5E+16 ohms·cm
Dielectric strength	3.00mm	IEC 60243-1	23 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		ASTM D257/IEC 60093	5×1016 Ω.cm
Volume resistivity	Volume resistivity	3mmt	ASTM D-257	5×10 Ω.cm
Dielectric strength	2mmt	ASTM D-149	23 MV/m

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ISO 2039-2	100

Supplementary Information	Test Condition	Test Method	Test Result
ColourNumber			EF2001/ED3002

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT DURANEX® 3300 JAPAN POLYPLASTIC

Material Description

Technical Data Sheet Compare

Technical Data Sheet