PEEK

PEEK VICTREX® 90GL30 VICTREX UK

279

Unit Price:US$ 68,926 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	400°C	ISO 11443	200 Pa·s

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1U	45 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	45 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	2.0mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2	12000 Mpa
bending strength	275°C	ISO 178	75.0 Mpa
Compressive stress	23°C	ISO 604	250 Mpa
	Compressive stress	120°C	ISO 604	160 Mpa
	Compressive stress	Compressive stress	250°C	ISO 604	55.0 Mpa
tensile strength	Break,23°C	ISO 527-2	195 Mpa
	tensile strength	Break,125°C	ISO 527-2	130 Mpa
		tensile strength	Break,175°C	ISO 527-2	80.0 Mpa
			tensile strength	Break,225°C	ISO 527-2	60.0 Mpa
			tensile strength	tensile strength	Break,275°C	ISO 527-2	45.0 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.4 %
Bending modulus	23°C	ISO 178	11500 Mpa
bending strength	23°C	ISO 178	290 Mpa
	bending strength	125°C	ISO 178	230 Mpa
	bending strength	bending strength	175°C	ISO 178	115 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	335 °C
Glass transition temperature		ISO 11357	143 °C
Melting temperature		ISO 11357-3	343 °C
Linear coefficient of thermal expansion	MD:<143°C	ISO 11359-2	2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:>143°C	ISO 11359-2	2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:<143°C	ISO 11359-2	4.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:>143°C	ISO 11359-2	1.1E-04 cm/cm/°C
thermal conductivity	23°C9	ISO 22007-4	0.30 W/m/K
thermal conductivity	thermal conductivity	23°C10	ISO 22007-4	0.35 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Spiral flow length	--5	Internal Method	18.5 CM
Spiral flow length	Spiral flow length	--6	Internal Method	22.0 CM
Shrinkage rate	TD	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30 %
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	100°C，Saturation	ISO 62	0.450 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	23°C,1MHz	IEC 60250	4E-03
Compared to the anti leakage trace index		IEC 60112	V
Volume resistivity		IEC 60093	1E+16 ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	23 KV/mm
Dielectric constant	23°C,1kHz	IEC 60250	3.30

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD,23°C	ISO 868	87

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEEK VICTREX® 90GL30 VICTREX UK

Material Description

Technical Data Sheet Compare

Technical Data Sheet